| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
| 基本性能 | 熔體流動速率 | 200℃，5000g | ASTM D-1238 | 4.6 | g/10min |
| 物理性能 | 比重 | 23℃(73?H) | ASTM D-792 | 1.19 | --- |
| 機械性能 | 洛氏硬度 | 23℃(73?H) | ASTM D-785 | 102 | R Scale |
| IZOD沖擊強度 | 1/4",6.35mm,23℃(73?H) | ASTM D-256 | 20(196)(3.67) | kgf.cm/cm(J/m)(Ft-lbs/in) |
| 拉伸強度 | 1/8",50mm/min,23℃(73?H) | ASTM D-638 | 435(42.6)(6.19) | kgf/cm2(MPa)(PSI×103) |
| 彎曲強度 | 1/8"×1"×4"bar,15mm/min,23℃(73?H) | ASTM D-790 | 715(70.1)(10.17) | kgf/cm2(MPa)(PSI×103) |
| 彎曲械量 | 1/8"×1"×4"bar,15mm/min,23℃(73?H) | ASTM D-790 | 24000(2.35)(3.41) | kgf/cm2(GPa)(PSI×103) |
| 熱 性 能 | 熱變形溫度 | 1/2"×1/2"×5"bar,18.6kg/cm2(264PSI) | ASTM D-648 | 78(172) | ℃(?H) |
| UL燃燒等級 | file NO:E206417 C-UL CSA LS 103112,1/8"thickness | UL 94 | HB | --- |
| UL燃燒等級 | file NO:E206417 C-UL CSA LS 103112,1/16"thickness | UL 94 | HB | --- |